• Powder Coating Used Zinc Flake Powder
  • Powder Coating Used Zinc Flake Powder
Powder Coating Used Zinc Flake Powder
  • China
  • 15-20 days
  • 80mt/m

1. Particle size as D50 about 11-13um.
2. Zinc flake powder is produced by dry producing method, with the nature of Longer salt-spray test time than spherical zinc powder More slowly sediment than the spherical zinc powder, better anti-corrosion effect than spherical zinc powder ,etter dispersion effect and better metallic white brightness, stable quality control for each producing lot enables its good quality.

Powder Coating Used Zinc Flake Powder

Product name: Zinc Flake Powder for Powder Coating and Dacromet


Appearance: Lamellar Metallic Silver Gray Powder


Technology: Dry method and high-energy ball milling technology, multi-coated layer processing;


Advantages: Better dispersion, longer salt fog time, slowly sedimentation in the coating material


Application: Daceomet/Geomet technology, Zinc-Cr Coating material,Powder coating and painting for Boats, Warships, Automotive parts, Vehicle, Iron tower and the like;


Chemical property and features:

1.In electro-chemistry: compared to the base metal Fe being protected, the Zn will be changed into solution in electrolyte to show the effectiveness, even the base metal being exposed because of the damage of the coating layer;

2.Sealing and tightness: the corrosion of the zinc powder (ZnCO3 and Zn(OH)2) deposits among the voids of the small zinc particles as filling stuff of the pigment, the electro-insulation makes it show the natures as sealing effectiveness;

3.Shielding natures: the lamellar powder shows parallel line in the surface of the coating film, as well as overlap and cross each other, which makes the water or corrosion medium difficult to be permeated that shows the anti-corrosion effectiveness.

 

Zinc Flake Powder for Dacromet/Geomet Coating:

Grade

Average Particle Size

D50(um)

Thickness of the

zinc flake (um)

Water Covering (min cm²/g±10%)

Bulk Density

(g/cm3)

Packaging

(N.W./KG

Steel Barrel)

D100

17-19

0.15-0.4

≥3500

0.8

25

D200

11-13

0.1-0.3

≥5000

0.75

25

D200A

9-11

0.1-0.2

≥6000

0.73

25

D300

4-5

0.1-0.2

≥8000

0.7

25


Zinc Flake Powder For Zinc Rich Paint and Coating:

Grade

Average Particle Size

D50(um)

Thickness of the

zinc flake (um)

Water Covering (min cm²/g±10%)

Bulk Density

(g/cm3)

Packaging

(N.W./KG

Steel Barrel)

F100

17-19

0.2-0.5

≥3000

0.85

25

F200

11-13

0.15-0.4

≥4000

0.8

25

F300

4-5

0.1-0.3

≥7000

0.75

25

N400

2-3

0.02-0.1

≥12000

0.6

20


 zinc powder